Synthesis of Ordered Mesoporous Carbon Using MCM-41 Mesoporous Silica as Template

摘要:

文章预览

Mesoporous carbon with high surface area and ordered structure was synthesized via a nanocasting process using mesoprous MCM-41 silica as a template and sucrose as a carbon precursor. Sample was characterized by XRD, SEM, TEM and nitrogen adsorption. The results show that the templated carbon has a BTE surface area ∼1200 m2/g, a pore volume ∼1.0 cm3/g, and a bimodal porosity centered at around 4 nm and 46 nm.

信息:

期刊:

主题:

编辑:

Masayuki Nogami, Riguang Jin, Toshihiro Kasuga and Wantai Yang

页数:

543-546

DOI:

10.4028/www.scientific.net/AMR.11-12.543

引用:

C. F. Lin et al., "Synthesis of Ordered Mesoporous Carbon Using MCM-41 Mesoporous Silica as Template", Advanced Materials Research, Vols. 11-12, pp. 543-546, 2006

上线时间:

February 2006

输出:

价格:

$35.00

[1] T. Kyotani: Carbon Vol. 38 (2000), p.269.

[2] J. Lee, S. Han and T. Hyeon: J. Mater. Chem. Vol. 14 (2004), p.478.

[3] A.H. Lu, W. Schmidt, N. Matoussevitch, H. Bonnermann, B. Spliethoff, B. Tesche, E. Bill, W. Kiefer and F. Schuth: Angew. Chem. Int. Ed. Vol. 43 (2004) p.4303.

DOI: 10.1002/anie.200454222

[4] C.M. Yang, C. Weidenthaler, B. Spliethoff, M. Mayanna and F. Schuth: Chem. Mater. Vol. 17 (2005), p.355.

[5] A.H. Lu, W.C. Li, W. Schmidt and F. Schuth: Microporous Mesoporous Mater. Vol. 80 (2005), p.117.

[6] A.B. Fuertes and S. Alvarez: Carbon Vol. 42 (2004), p.3049.

[7] A.H. Lu, A. Kiefer, W. Schmidt and F. Schuth: Chem. Mater. Vol. 16 (2004), p.100.

[8] T.W. Kim, I.S. Park and R. Ryoo: Angew. Chem. Int. Ed. Vol. 42 (2003), p.4375.

[9] S.H. Joo, S. Jun and R. Ryoo: Microporous Mesoporous Mater. Vol. 44-45 (2001), p.153.

[10] J. Lee, S. Yoon, S.M. Oh, C.H. Shin and T. Hyeon: Adv. Mater. Vol. 12 (2000), p.359.

[11] C.H. Kim, D.K. Lee and T.J. Pinnavaia: Langmuir Vol. 20 (2004), p.5157.

[12] B. Tian, S.N. Che, Z. Liu, X.Y. Liu, W.B. Fan, T. Tatsumi, O. Terasaki and D.Y. Zhao: Chem. Commun. (2003), p.2726.

[13] Q. Cai, Z.S. Luo, W.Q. Pang, Y.W. Fan, X.H. Chen and F.Z. Cui: Chem. Mater. Vol. 13 (2001), p.258.

为了查看相关信息, 需 Login.