Reaction between Carbon Dioxide and Mechanically Activated Metal Powder

摘要:

文章预览

A fundamental study on the reaction between CO2 and mechanically activated metal powders has been conducted. In this research, the behavior and mechanism of CO2 reaction under various grinding conditions were investigated to fix and reduce CO2. The powder used was placed inside a grinding vessel, and was ground together with the SUJ2 balls in CO2 atmosphere. It was found that only the adsorption of CO2 gas on the ground samples was observed, whereas the decomposition of CO2 was not occurred. The CO2 adsorption increased proportionally with the increase in the grinding speed, weight of sample and number of SUJ2 balls. Furthermore, the CO2 adsorption increased with the decrease in the standard free energy of formation of each metal oxide. The morphology of the sample observed by SEM showed that the samples were not crushed into finer particles, but were only grazed on the sample’s surface. Therefore, it can be said that the CO2 can be adsorbed on the mechanically activated samples by using the centrifugal type ball mill, but in order to enhance the amount of CO2 adsorption, another type of machine with higher grinding intensity should be considered.

信息:

期刊:

编辑:

Xie Yi and Li Mi

页数:

799-803

DOI:

10.4028/www.scientific.net/AMR.129-131.799

引用:

N. H. Muhd Nor et al., "Reaction between Carbon Dioxide and Mechanically Activated Metal Powder", Advanced Materials Research, Vols. 129-131, pp. 799-803, 2010

上线时间:

August 2010

输出:

价格:

$38.00

[1] T.Y. Dong: Advanced Materials Research 108-111 (2010) p.909.

[2] Z. Huang, X. Ding, H. Sun, S. Liu: Mater. Sci. Forum 650 (2010) p.9.

[3] S. Bachu, J.J. Adams: Energy Conversion and Management 44 (2003) p.3151.

[4] H. Marusawa, Y. Saito: Key Engineering Materials 350 (2007) p.143.

[5] S. Eloneva, S. Teir, J. Salminen, C.J. Fogelholm and R. Zevenhoven: Energy 33 (2008) p.1461.

[6] S. Yokoyama, R. Sato, M.N.N. Hisyamudin and M. Umemoto: ISIJ Int. 50 No. 3 (2010) p.482.

[7] M.N.N. Hisyamudin, S. Yokoyama and M. Umemoto: Mater. Sci. Forum 654-656 (2010), p.2927.

[8] M.N.N. Hisyamudin, S. Yokoyama, M. Kawakami and M. Umemoto: Pow. Tech. 196 (2009) p.156.

[9] S. Yokoyama, M.N.N. Hisyamudin and S. Hirano: Mater. Sci. Forum 654-656 (2010) p.2923. (a) (b) 100 µm 10 mm CO2.

为了查看相关信息, 需 Login.