Preparation and Test of Polyurethane Foam Composites with Alkali Lignin/Renewable PUF

摘要:

文章预览

The polyurethane foam composite was prepared by alkali lignin and renewable polyurethane foam (PUF). The thermal stability as well as compression property was studied. It was obtained from the TG curve and the DTG curve that the initial decomposition temperatures of polyurethane foam composites with 10% renewable PUF and without renewable PUF were 560.25K and 574.13K,respectively, which showed the renewable PUF affacted the thermal stability of the polyurethane foam composite. The compressive strength (σ10)was from 203kPa to 125 kPa , which were affacted by the dose of the renewable PUF.

信息:

期刊:

编辑:

Jinglong Bu, Zhengyi Jiang and Sihai Jiao

页数:

1167-1170

引用:

C. Y. Li and L. L. Liu, "Preparation and Test of Polyurethane Foam Composites with Alkali Lignin/Renewable PUF", Advanced Materials Research, Vols. 150-151, pp. 1167-1170, 2011

上线时间:

October 2010

输出:

价格:

$38.00

[1] Y.S.T. Snakamura, M. T Sungusia and T. S Sawada: J. BIOSU. BIOENC. Vol 88 (1999) , p.41.

[2] E.A. Borges da Silvaa, M. Zabkovaa and J.D. Araújoa : ChERD. Vol 87 ( 2009 ), p.1276.

[3] C. Y Li, L. L Liu and H. Y Zhang, C.N. Patent 101012332, 08-08, 666. (2007).

[4] H. Wang, H. Z Chen: J. Chinese Institute of Chemical Engineers. Vol 38 (2007), p.95.

[5] Y.S. T NakmuraAKAMURA, M. G Sungusia T. T Sawada and M.S. K Kuwaharaza: Thermochimica Acta. Vol 431 (2005), p.155.

[6] Y. T Liu , J. X Zhang, D. W Yin and B Lv:J. New Chemica Materials. Vol 37(2009), p.3.

[7] L. L Liu , C. Y Li : Chemistry and Industry of Forest Products. Vol 30 (2009), p.47.

[8] Y. M Xie, R. J Gu and H Wu: Paper Chemicals. Vol 3 (2000) , p.1.

[9] Y. Z Tao ,Y. T Guan: J. Cellulose Science and Technology . Vol 11 (2003), p.42.