Co-Deposition of Binary Particles during Slip Casting Process



Co-deposition of silicon carbide particles and carbon (or carbon sources) particles is essential for preparation of reaction bonded silicon carbide (RBSC) products by slip casting. The way of co-depositing of silicon carbide particles and carbon particles during slip casting process, and the influence of composition of raw particles on particle co-depositing in green bodies were studied. The experiment results show: 1.Co-deposition of binary particles is greatly affected by particle size distribution, and large proportion of rigid SiC particles increases the difficulty in demoulding procedure because of small shrinkage; 2. Dispersants in deposited cake trend to enrich at the surface in contact with mould wall, while this enrichment of dispersant has little effect on mechanical performance of RBSC products; 3. Sharp edges on surface of raw particles could result to friction among particles, which afford strength to green bodies but prevent particles packing more closely.




Zhengyi Jiang, Shanqing Li, Jianmin Zeng, Xiaoping Liao and Daoguo Yang




Y. Li and Y. Qiu, "Co-Deposition of Binary Particles during Slip Casting Process", Advanced Materials Research, Vols. 189-193, pp. 2917-2920, 2011


February 2011





[1] Sanjay Agarwal, P. Venkateswara Rao: Inter. J. Mach. Tools. & Man., Vol. 50 (2010), p.1077.

[2] JMF Ferrira, Diz H M M: Ceram. Inter., Vol. 25(1999), p.491.

[3] Rolf Janssen, Sven Scheppokat, Nils Claussen: J. Euro. Cera. Soc., Vol. 28 (2008), p.1369.

[4] Yuan Li, Jing Lin, Jiqiang Gao, et al.: Mater Sci. Eng. A, Vol. 483-484 (2008), p.676.

[5] Qingwei Huang, Guanjun Qiao, et al.: Rare Metals Eng. Vol. 30 (2001), p.150.

[6] Wilks, Edward S.: Industrial polymers handbook (In Chinese), Chemical Industrial Publications, Beijing, China, (2006).

[7] U. Paik and H. Cheo: Mater. Sci. Eng. A, Vol. 334 (2002), p.267.