Kinetics on the Desiliconization during Alkaline Leaching of Titanium Slag

摘要:

文章预览

In order to reduce the silicon content to the maximum allowed value for the production of high-purity titanium dioxide, a hydrometallurgical process on the desiliconization during alkaline leaching of titanium slag under atmospheric pressure was studied. The effect of leaching temperature, initial NaOH concentration, leaching time and mass ratio of alkali to slag, on the efficiency of silicon removal were investigated. The results show that when the mass concentration of NaOH is 30%, mass ratio of alkali to slag 3:1, the leaching temperature 120°C and the retention time about 120min, the content of silicon in solid is reduced to 0.45%. Simultaneously, the content of aluminum is reduced to 1.62%, without affecting the content of titanium. The kinetics on the desiliconization during alkaline leaching of titanium slag was carried out. The results show that under the leaching parameters mentioned above, the apparent activation energy is calculated to be 45.43kJ/mol.

信息:

期刊:

编辑:

Zhong Cao, Lixian Sun, Xueqiang Cao, Yinghe He

页数:

1322-1327

DOI:

10.4028/www.scientific.net/AMR.233-235.1322

引用:

J. H. Liu et al., "Kinetics on the Desiliconization during Alkaline Leaching of Titanium Slag", Advanced Materials Research, Vols. 233-235, pp. 1322-1327, 2011

上线时间:

May 2011

输出:

价格:

$35.00

[1] C. N. Rao and S. R. Yoganarasimhan and P. A. Faeth: Trans. Farad. Soc. Vol. 57(1961), p.504.

[2] Z. H. Chen and C. H. Liu: Manufacture and Application Technology of Titanium Dioxide Pigment, 1st ED( Chemical Industry Press, China 2006).

[3] G. Buxban and G. Pfaff: Industrial Inorganic Pigments. (Wiley-VCH, Weinheim, Germany 2005).

[4] H. B. Juergen, B. Andrejs and E. Robert: TiO2 pigment technology: a review. Prog. Org. Coat. Vol. 20(1992), p.105.

[5] Tianyan X., Lina W., Tao Q., Jinglong C., Jingkui Q. and Changhou. L.: Decomposition kinetics of titanium slag in sodium hydroxide system. Hydrometallurgy Vol. 95(2008), p.22.

DOI: 10.1016/j.hydromet.2008.04.004

[6] G. Mazzocchitti, I. Giannopoulou, and D. Panias: Silicon and aluminum removal from ilmenite concentrates by alkaline leaching. Hydrometallurgy Vol. 96(2009), p.327.

DOI: 10.1016/j.hydromet.2008.12.001

[7] B. Yang, J.G. Wang, Y.F. Zhang, and Y. Zhang: Pre-desiliconization of a Bauxite Ore through Leaching by High Concentration NaOH Solution under Atmospheric Pressure. The Chinese Journal of Process Engineering. Vol. 7(2007), p.922.

[8] E. Matijevic F., Mangravite and A. Cassell: Stability of Colloidal Silica: IV. the Silica-Alumina System. Colloid Interface Sci. Vol. 4(1974), p.560.

DOI: 10.1016/0021-9797(71)90214-1

[9] R. Fricke and P. Jucaitis: Unter suchungen uber die Gleichgewichte in den System Al2O•NaOH and AlO•KO•HO. Z. Anorg. Allg. Chem. Vol. 191(1930), p.129.

DOI: 10.1002/zaac.19301910117

[10] Panagiotopoulou Ch., Kontori, E., Perraki Th. and Kakali G.: Dissolution ofaluminosilicate minerals and by-products in alkaline media. Journal of Materials Science Vol. 42(2006), p.2967.

DOI: 10.1007/s10853-006-0531-8

为了查看相关信息, 需 Login.