Surface Roughness of Cu-Be Alloy (C17200) Rod Alloy Produced by Horizontal Type Continuous Casting Process

摘要:

文章预览

Cu-Be alloy (C17200) rod having diameter of 23.5mm was produced by a vacuum continuous casting method at furnace temperature range of from 1240°C to 1260°C with casting speed range of from 35mm/min to 103mm/min. When the furnace temperature was 1240°C and 1250°C, Cu-Be alloy rod without fracture could successfully produced at high casting speed of 103mm/min. However, when the furnace temperature was 1260°C, the breakout occurred at casting speed faster than 78mm/min. Surface roughness (Ra) increased with increasing not only a furnace temperature but also a casting speed.

信息:

期刊:

编辑:

Young Won Chang, Nack J. Kim and Chong Soo Lee

页数:

551-554

引用:

S. K. Lee et al., "Surface Roughness of Cu-Be Alloy (C17200) Rod Alloy Produced by Horizontal Type Continuous Casting Process", Advanced Materials Research, Vols. 26-28, pp. 551-554, 2007

上线时间:

October 2007

输出:

价格:

$38.00

[1] A. Woodcraft, R.V. Sudiwala, and R.S. Bhatia, Cryogenics, 41(2001), 603-606.

[2] K. Laue and H. Stenger, Extrusion, second edition, (1976).

[3] B.S. You, C.D. Yim, and S.H. Kim, Mater. Sci. Eng. A 413-414(2005), 139-143.

[4] H.R. Muller, Continuous casting, (2006).

从Crossref获取数据。
这可能需要一些时间来加载。