Effect of Nano Silica on the Sinterability of Hydroxyapatite Dense Bodies

摘要:

文章预览

The effects of adding a small amount of nano silica in hydroxyapatite (HA) on the sinterability and mechanical properties of hydroxyapatite were studied. The starting HA powder was synthesized using a novel wet chemical precipitation method. Different amount of silica powder was mechanically mixed with the synthesized HA. The green samples were subsequently cold isostatically pressed at 200 MPa. Sintering in air was accomplished by firing the green samples at temperatures ranging from 1050°C to 1250°C. Sintered samples were analyzed to determine phase composition and mechanical properties. The XRD analysis revealed that with increasing the amount of silica in the HA powder, decomposition of HA to TCP occurred at sintering temperature higher than 1050°C. The bulk density of all silica-doped samples decreased through the temperature range studied. In agreement with the bulk density trend, the increasing silica additives in HA depleted the Young’s modulus and Vickers hardness of the HA body. The study revealed that the addition of silica have an adverse effect on the sintered properties of hydroxyapatite bioceramics.

信息:

期刊:

编辑:

M.S.J. Hashmi, S. Mridha and S. Naher

页数:

1832-1838

DOI:

10.4028/www.scientific.net/AMR.264-265.1832

引用:

R. Tolouei et al., "Effect of Nano Silica on the Sinterability of Hydroxyapatite Dense Bodies", Advanced Materials Research, Vols. 264-265, pp. 1832-1838, 2011

上线时间:

June 2011

输出:

价格:

$35.00

[1] R.Z. LeGeros, J.P. LeGeros. Dense hydroxyapatite. In: Hench, L.L., Wilson, J. (Eds. ), an Introduction to Bioceramics. World Scientific, Singapore, (1993), p.139 (Chapter 9).

DOI: 10.1142/9789814317351_0009

[2] G. Muralithran, S. Ramesh. The effect of MnO2 addition on the sintering behavior of Hydroxyapatite. Biomedical Engineering Application Basis, Vol. 12, (2000), 43-48.

[3] W. Suchanek, M. Yoshimaru. Processing and properties of hydroxyapatite-based biomaterials for use as hard tissue replacement implants. Journal of Materials Research, Vol. 13, (1998), 94-117.

DOI: 10.1557/jmr.1998.0015

[4] T. V. Safronova, V. I. Putlyaev, M. A. Shekhirev, Y.D. Tretyakov, A.V. Kuznetsov. Densification additives for hydroxyapatite ceramics. Journal of the European Ceramic Society, Vol. 29, (2009), 1925-(1932).

DOI: 10.1016/j.jeurceramsoc.2008.12.012

[5] Suchanek, W., Yashima, M., Kakihana, M., and Yoshimura, M., Hydroxyapatite ceramics with selected sintering additives. Biomaterials, Vol. 18, (1997), 923-933.

DOI: 10.1016/s0142-9612(97)00019-7

[6] S. Ramesh, W. H. Yeo, K. L. Aw, C. Y. Tan. The effect of Bismuth oxide on the sinterability of Hydroxyapatite..

[7] I. R. Gibson. Effect of Silicon Substitution on the Sintering and Microstructure of Hydroxyapatite. Journal of American Ceramic Society, Vol. 85, (2002)2771-77.

[8] S. Ramesh, Patent No. 20043325. Malaysia. (2004).

[9] ASTM E1876-97, Annual Book of ASTM Standards, (1998).

[10] J. Xu, K. Khor, Chemical analysis of silica doped hydroxyapatite biomaterials consolidated by a spark plasma sintering method. Journal of Inorganic Biochemistry, Vol. 101, (2007), 187-195.

DOI: 10.1016/j.jinorgbio.2006.09.030

[11] S. Ramesh, C. Y. Tan, K. L. Aw, W. H. Yeo, M. Hamdi, I. Sopyan, W. D. Teng. Sintering behaviour of hydroxyapatite bioceramics, The Medical Journal of Malaysia, Vol. 63, (2008), 89-90.

为了查看相关信息, 需 Login.