Anticorrosion Conversion Coating Content Lanthanum and Phosphate on Foam Mg Alloy

摘要:

文章预览

Foam magnesium alloy was an idea substitute of hard tissue of human bodies because its elasticity module was close to the bone of human. In the paper, foam degradable magnesium alloys were prepared by “Press-Dissolution-Vacuum sintering-Hot treatment-Aging” powder manufacturing process firstly. Then samples were coated by immersion in a bath containing phosphate and rare earths lanthanum. Results show that, Mg-0.9Mn foam magnesium alloys after hot treatment had better anticorrosion performance; and coated foam magnesium alloys form the bath with phosphate lanthanum chloride had lower rate of degradation.

信息:

期刊:

编辑:

Jianzhong Wang and Jingang Qi

页数:

211-214

DOI:

10.4028/www.scientific.net/AMR.299-300.211

引用:

L. Y. Niu et al., "Anticorrosion Conversion Coating Content Lanthanum and Phosphate on Foam Mg Alloy", Advanced Materials Research, Vols. 299-300, pp. 211-214, 2011

上线时间:

July 2011

输出:

价格:

$35.00

[1] C. E. Wen, , Y. Yamada, K. Shimojima, Y. Chino, H. Hosokawa and M. Mabuchi : Materials Letters. Vol. 58 (2004), p.357.

[2] ZHENG R. F, LIANG C. H: Materials and corrosion Vol. 58 (2007), p.193.

[3] WANG Lishi, CAI Qizhou, WEI Bokang, et al : Trans Nonferrous Met Soc China Vol. 15 (2005), p.777.

[4] LI Jianzhong, TIAN Yanwen, CUI Zuoxing, and HUANG Zhenqi: Rare Metals Vol. 27 (2008), p.50.

[5] Kwo Zong Chong and Teng Shih Shih: Materials Chemistry and Physics Vol. 80(2003), p.191.

[6] G.Y. Li, J.S. Lian, L.Y. Niu, et al : Advanced Engineering Materials Vol. 8 (2006), p.123.

[7] Wanqiu Zhou, Dayong Shan, En-Hou Han.: Corrosion Science Vol. 50(2008), p.329.

为了查看相关信息, 需 Login.