Melting Behaviour and Surface Structure of Glazes Containing Wollastonite and Dolomite



The influence of wollastonite and dolomite on melting behaviour and crystallization was studied for 25 raw glazes. The melting behaviour was observed by hot-stage microscopy. The glazes were also fired industrially both in a fast-fired gas kiln for floor tiles (50 min) and in a traditional gas kiln for sanitaryware (25 hours). The surface composition and structure of the glazes were studied by SEM/EDXA. The crystalline phases in the glazes were identified by XRD. Main crystalline phases found in the glazes were wollastonite and diopside. Fusibility and surface structure on the raw glazes containing wollastonite and dolomite as raw materials depended both on the total content and the ratio of CaO and MgO in the glaze. Low content of alkaline earths gave incomplete fusion, while high content gave extensive crystallization. The results can be applied to tailor raw glaze compositions for a desired surface structure to be fired at a certain fusion temperature.







T. Kronberg et al., "Melting Behaviour and Surface Structure of Glazes Containing Wollastonite and Dolomite", Advances in Science and Technology, Vol. 45, pp. 590-595, 2006


October 2006




[1] T. Manfredini: Key Eng. Mat. Vols 206-213 (2002), p (2031).

[2] G. Baldi, E. Generali, C. Leonelli, T. Manfredini, G.C. Pellacani, C. Silligardi: J. Mat. Sci. 30 (1995), p.3251.

[3] M.L. Övecoglu, B. Kuban, H. Özer: J. Eur. Ceram. Soc. 17 (1997), p.957.

[4] F.J. Torres, J. Alarcon: J. Non-Cryst. Solids: 347 (2004), p.45.

[5] F.J. Torres, J. Alarcon: J. Eur. Ceram. Soc. 25 (2005), p.349.

[6] A.M. Ferrari, L. Barbieri, C. Leonelli, T. Manfredini, C. Siligardi, A.B. Corradi: J. Am. Ceram. Soc. 80 (1997), p.1757.

[7] F.J. Torres, J. Alarcon: J. Am. Ceram. Soc. 87 (2004), p.1227.

[8] F.J. Torres, J. Alarcon: J. Eur. Cer. Soc. 23 (2003), p.817.

[9] J.R. Taylor, A.C. Bull: Ceramics Glaze Technology (Oxford, Pergamon Press 1986).

[10] L. Fröberg, T. Kronberg, L. Hupa, M. Hupa: J. Eur. Ceram. Soc in print.

[11] H. Scholze: Ber. Dtsch. Keram. Ges. 39 (1962) p.63.

[12] M. Paganelli: Ind. Ceram. 17 (1997) p.69.

[13] M.J. Pascual, L. Pascual and A. Duran: Phys. Chem. Glasses 42 (2001) p.61.

[14] T. Kronberg, L. Hupa, K. Fröberg: Advances in Science and Technology, 34 (2003) p.55.

[15] M. Ahmed, D.A. Earl: Am. Cer. Soc. Bull. 81 (2002) p.47.

[16] G.W. Morey: J. Am. Ceram. Soc, 13 (1930), p.714.

[17] R.A. Eppler, R.D. Eppler: Glazes and Glaze Coatings (Westerville, 2000).