A New Dewaxing Method and its Effect on the Properties of Low-Pressure Injection Molded Ceramics



A new dewaxing method for low-pressure injection molded ceramics is presented. Supercritical extraction with carbon dioxide was used to remove paraffin wax from the ceramic green parts. The composition of organic additives for low-pressure injection molding feedstock and the extraction condition for the green parts were investigated. Moreover, the properties of sintered ceramic samples dewaxed by supercritical carbon dioxide were compared with those by thermal dewaxing. The results show that the new binder system containing 50wt% paraffin wax, 35% bee wax and 15% stearic acid fulfills the requirements of both low-pressure injection molding feedstocks and supercritical dewaxing, where the feedstock has high fluidity, low viscosity and quick solidification. The efficient extraction condition for supercritical dewaxing from the green parts is at 30MPa pressure and 45°C. Under this condition, defect free ceramic green parts can be obtained. Dewaxing methods have significant influence on the properties of sintered parts. The mechanical properties of the sintered sample can be improved by supercritical dewaxing. With this method, the bending strength of sintered samples (σ = 331.6 MPa) is higher than that obtained by thermal treatment (σ = 312.3MPa). The sintered samples dewaxed by supercritical CO2 have shown the property of higher density and less distortion compared to the thermal dewaxing method. Moreover, with supercritical extraction the dewaxing time can be reduced to about one tenth of the time required by thermal dewaxing.




Wei Pan and Jianghong Gong




Y. Wu et al., "A New Dewaxing Method and its Effect on the Properties of Low-Pressure Injection Molded Ceramics", Key Engineering Materials, Vols. 336-338, pp. 1012-1016, 2007


April 2007




[1] D.M. Liu: Ceram. Int. Vol. 25 (1999), p.582.

[2] H.M. Shaw and M.J. Edirisinghe: Am. Ceram. Soc. Bull. Vol. 72 (1993), p.94.

[3] W.J. Tseng and C.K. Hsu: Ceram. Int. Vol. 25 (1999), p.461.

[4] G. Brunner: Gas Extraction: An Introduction to Fundamentals of Supercritical Fluids and the Application to Separation Processes. (New York: Springer, 1994), p.179.

[5] A. Galia, A. Argention, O. Scildone, et al.: Supercrit. Fluids Vol. 24 (2002), p.7.

[6] R.M. German: Int. J. Powder Metall. Vol. 23 (1987), p.237.

[7] P.D. Calvert and M.J. Cima: J. Am. Ceram. Soc. Vol. 73 (1990), p.575.

[8] M.R. Barone and J.C. Ulicny: J. Am. Ceram. Soc. Vol. 73 (1990), p.3323.

[9] V.N. Shukla and D.C. Hill: J. Am. Ceram. Soc. Vol. 72 (1989), p.1797.