Slip Casting of Green Compact of SiAlON Multiphase Ceramics from River Sand

摘要:

文章预览

Green compact containing Yellow River sand and several additives was prepared by slip casting and the as-made compact was used to synthesize SiAlON multiphase ceramics by carbothermal reduction nitridation. The processing parameters of slip casting including the type and concentration of dispersant, solid loading, ball milling time, pH value and particle size distribution were optimized by orthogonal experiments. The results indicated that the raw materials could disperse uniformly in the suspension under the use of the mixed dispersant of skip liquid (SL, PT) and sodium carboxymethylcellulose (CMC). The green body with high bulk density of 1.86 g·cm-3 was obtained. After sintered in flowing N2, the compact could transform to SiAlON multiphase ceramics.

信息:

期刊:

编辑:

Wei Pan and Jianghong Gong

页数:

1386-1389

DOI:

10.4028/www.scientific.net/KEM.336-338.1386

引用:

B. Xu et al., "Slip Casting of Green Compact of SiAlON Multiphase Ceramics from River Sand", Key Engineering Materials, Vols. 336-338, pp. 1386-1389, 2007

上线时间:

April 2007

输出:

价格:

$35.00

[1] X. Xu, M.I.L.L. Oliveira, R.L. Fu and J.M.F. Ferreira: J. Euro. Ceram. Soc. Vol. 23 (2003), p.1525.

[2] B. Basu, J. Vleugels, M. Kalin and O.V.D. Biest: Mater. Eng. Vol. 359 (2003), p.228.

[3] H.J. Zhang, W.C. Li and X.C. Zhong: NaihuoCailiao (Chinese) Vol. 34 (2000), p.137.

[4] J.G. Lee and I.B. Cutler: J. Am. Ceram. Soc. Vol. 58 (1979), p.869.

[5] A.L. Jennifer: J. Am. Ceram. Soc. Vol. 83 (2000), p.2341.

[6] L.H. Xu, Z.F. Cheng, F. Lian, T.Z. Wang and Y. Yao: Key Eng. Mater. Vol. 280-283 (2005). p.1675.

[7] T. Hotta, H. Abe, M. Naito, M. Takahashi, K. Uematsu and Z. Kato: Powd. Tech. Vol. 149 5), p.106.

[8] G.H. Ji , B.M. Yang and T. Liu: J. Shandong Uni. Tech. (Chinese) Vol. 18 (2004), p.102 Fig. 4 XRD pattern of sintered sample H26. Fig. 5 Microstructure of sintered sample H26.

为了查看相关信息, 需 Login.