Variations in the Compression Strength of Cylindrical Samples Made of Dense Hydroxyapatite



Dense bioceramics made of pure hydroxyapatite (HA) was prepared and characterized. The cylindrical samples were compacted from HA powders of diverse pretreatments; namely, from spray-dried HA, calcined HA and mixtures thereof. The samples were prepared by a hydraulic press under different compaction loads both with and without auxiliary compounds (a binder and a lubricant). Both the total mass and geometrical dimensions of the prepared cylinders were measured. Then, the cylindrical samples were sintered at 1200 °C for 4 hours. After cooling down to ambient temperature, the sintered cylinders were weighed and their geometrical dimensions were measured once again. Mass decreasing and the shrinkage degree were calculated as a result. Afterwards, the compression strength of the sintered cylinders was measured by an Instron 5587 machine. Preparation of dense HA bioceramics possessing the highest possible compression strength was the purpose of this study. The necessary processing parameters were discovered.





Guy Daculsi and Pierre Layrolle




S. V. Dorozhkin et al., "Variations in the Compression Strength of Cylindrical Samples Made of Dense Hydroxyapatite", Key Engineering Materials, Vols. 361-363, pp. 103-106, 2008


November 2007




[1] J.C. Elliott: Structure and chemistry of the apatites and other calcium orthophosphates. (Elsevier, Amsterdam 1994).

[2] S. Baklouti, J. Bouaziz, T. Chartier and J-F Baumard: J. Europ. Ceram. Soc. Vol. 21 (2001), p.1087.

[3] M. Uppalapati and D.J. Green: J. Amer. Ceram. Soc. Vol. 88 (2005), p.1397.

[4] T. Kraft, H. Riedel and O. Rosenfelder: Int. J. Powder Metall. Vol. 39 (2003), p.27.

[5] J.S. Reed: Principles of Ceramics Processing. 2nd Edition. (Wiley-Interscience, New York 1995).