Gap Effect on the Heterogeneous Nucleation of Apatite on Thermally Oxidized Titanium Substrate

摘要:

文章预览

Apatite formation on the surface of materials in body environment is an essential condition to show osteoconduction after implantation in bony defects. This study reports the novel technique for providing the apatite-forming ability to titanium metals by only controlling the spatial gap and thermal oxidation. Two pieces of titanium thermally oxidized at 400 °C were set together like V-letter with varied mouth opening. They showed the formation of apatite on both facing surface after exposure to a simulated body fluid (SBF) proposed by Kokubo and his colleagues, when the gap was less than approximately 600 μm. Moreover, specimens with micro-grooves of 500 μm in depth and 200-1000 μm in width was able to form apatite in SBF with in 7 days, after they were thermally oxidized at 400 oC. These results indicated that the titanium metals were provided with apatite-forming ability, i.e. osteoconduction, due to controlled gap with thermally oxidized surface. Hence, we conclude that bioactive titanium substrate showing osteoconduction can be produced by designed machining followed by thermal oxidation at an appropriate temperature.

信息:

期刊:

主题:

编辑:

Guy Daculsi and Pierre Layrolle

页数:

621-624

DOI:

10.4028/www.scientific.net/KEM.361-363.621

引用:

A. Sugino et al., "Gap Effect on the Heterogeneous Nucleation of Apatite on Thermally Oxidized Titanium Substrate", Key Engineering Materials, Vols. 361-363, pp. 621-624, 2008

上线时间:

November 2007

输出:

价格:

$35.00

[1] T. Kokubo, J. Ceram. Soc. Japan (Seramikkusu Ronbunshi), 99 (1991), p.965.

[2] H. M. Kim, J. Ceram. Soc. Japan, 109 (2001), p. S49.

[3] T. Kokubo, H. M. Kim, M. Kawashita, T. Nakamura, J. Mater. Sci.: Mater. Med., 15 (2004), p.99.

[4] X. X. Wang, W. Yan, S. Hayakawa, K. Tsuru, A. Osaka, Biomaterials, 24 (2003), p.4631.

[5] T. Kokubo, H. Kushitani, S. Sakka, T. Kitsugi, T. Yamamuro, J. Biomed. Mater. Res., 24 (1990), p.721.

[6] T. Kokubo, H. Takadama, Biomaterials, 27 (2006), p.2907.

[7] C. Ohtsuki, H. Kushitani, T. Kokubo, S. Kotani and T. Yamamuro, J. Biomed. Mater. Res. 25 (1991), p.1363.

[8] X. X. Wang, S. Hayakawa, K. Tsuru, A. Osaka, J. Biomed. Mater. Res. 54 (2001), p.172.

为了查看相关信息, 需 Login.