Effects of Rare Earth Oxides on Microstructures and Properties of Magnesia Refractories

摘要:

文章预览

The effects of Y2O3, La2O3 and Nd2O3 on the sintering, microstructure and mechanical properties of magnesia refractories were investigated. Addition of rare earth oxide (ReO) to magnesia refractories increases the bulk density, decreases the porosity and improves the mechanical strength of the refractories. The improved sinterability was attributable to the vacancies generation associated with the solid-solution reactions between MgO and ReO. In the samples with ReO, rare earth silicate phases form at magnesia grain boundaries, providing additional bonding between magnesia grains and between magnesia grains and matrix. Consequently, the samples with ReO showed much higher high temperature strengths than those without ReO.

信息:

期刊:

编辑:

Wei Pan and Jianghong Gong

页数:

1158-1160

引用:

B. G. Zhang et al., "Effects of Rare Earth Oxides on Microstructures and Properties of Magnesia Refractories", Key Engineering Materials, Vols. 368-372, pp. 1158-1160, 2008

上线时间:

February 2008

输出:

价格:

$38.00

[1] A.G.M. Othman: Br. Ceram. Trans. Vol. 102 (2003), p.265.

[2] A.G.M. Othman and N.M. Khalil: Ceram. Int. Vol. 31 (2005), p.1117.

[3] C.H. Xu and X. Ai: Mater. Rev. Vol. 11.

[5] (1997), p.46.

[4] K.W. Chae and D.Y. Kim: J. Am. Ceram. Soc. Vol. 76 (1993), p.1857.

[5] K. Biswas, G. Rixecker and F. Aldinger: J. Eur. Ceram. Soc. Vol. 23 (2003), p.1099.

[6] Y.J. Liu, J.J. Sun and Y.Z. Wang: Bull. Chin. Ceram. Soc. Vol. 23.

[2] (2004), p.89.

[7] R. Sarkar, H.S. Tripathi, and A. Ghosh: Mater. Lett. Vol. 58 (2004), p.2186. Fig. 2 XRD patterns of the samples MY and MP fired 3h at 1600°C.