Prediction of Residual Stress Relaxation of Shot Peened 2024-T351 Aluminum Alloy: Part 2

摘要:

文章预览

The initial compressive residual stresses induced or inherent in a component will not remain stable during the life of the component, it relax and redistributed. In design of the component, it is important to consider the relaxation of residual stress phenomenon. In this study, equations to predict residual stress relaxation of 2024 T351 aluminium alloy specimens were proposed. The equations developed from the experimental data of 2024 T351 aluminium alloy specimens that were shot peened under three different shot peening intensities and undergoing cyclic tests for two load magnitudes for 1, 2, 10, 1000 and 10000 cycles. The residual stress, cold work and microhardness results were recorded after each cyclic load as well as the initial state. The presented model incorporates parameters including the degree of cold work, initial induced residual stress and the number of applied loading cycles.

信息:

期刊:

编辑:

Ahmad Kamal Ariffin, Shahrum Abdullah, Aidy Ali, Andanastuti Muchtar, Mariyam Jameelah Ghazali and Zainuddin Sajuri

页数:

1349-1354

引用:

O. S. Zaroog et al., "Prediction of Residual Stress Relaxation of Shot Peened 2024-T351 Aluminum Alloy: Part 2", Key Engineering Materials, Vols. 462-463, pp. 1349-1354, 2011

上线时间:

January 2011

输出:

价格:

$38.00

[1] Juijerm, P. and Altenberger, I.: Journal of Scripta Materialia. Vol. 55 (2006), p.1111.

[2] Niku-Lari, A.: Oxford: Pergamon Press, (1987).

[3] S. Kodama, in: Proceedings of the international conference Mechanical Behavior of Metals II, Society of Material Science, Kyoto, Japan, (1972), P. 111.

[4] Qui, Q. and Wang, R., in: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Partenkirchen, Germany, (1987), p.231.

[5] S. Han, T. Lee and B. Shin: Steel Res. Vol 73 (2002), p.414.

[6] W.Z. Zhuang and G.H. Halford: Int. J. Fatig. Vol. 23 (2001), p. S31.

[7] Omar Suliman Zaroog, Aidy Ali, and B. B. Sahari: Key Engineering Materials, in press.

DOI: https://doi.org/10.4028/www.scientific.net/kem.462-463.912

[8] Jhansale HR, Topper TH, in: Cyclic Stress–Strain Behavior Analysis, Experimentation, and Failure Prediction ASTM STP 519, American Society for Testing and Materials, (1973), p.246.

DOI: https://doi.org/10.1520/stp38034s