Effect of the Addition of Al Power on the Microstructure and Phase Constitution of Al2O3-MgO Composites Sintered at 1700°C under N2 Atmosphere

摘要:

文章预览

Al2O3-MgO-Al composites were prepared by sintering in carbon tube furnace at 1700°C under nitrogen atmosphere with tabular alumina, sintered magnesia and aluminum powder as raw materials. Effect of Al powder content on the porosity, microstructure and phase constitution of Al-Al2O3-MgO composites were investigated. The results show that the main phase was non-stoichiometric spinel solid solution, and a little AlN, AlON and MgAlON were detected by XRD. With Al power content increasing, the amount of the porosity and AlN, AlON and MgAlON around the porosity detected by SEM increased. These new phases enhance the combination of the large particles and the matrix.

信息:

期刊:

编辑:

Wei Pan, Jianghong Gong

页数:

341-344

引用:

J. J. Ma et al., "Effect of the Addition of Al Power on the Microstructure and Phase Constitution of Al2O3-MgO Composites Sintered at 1700°C under N2 Atmosphere", Key Engineering Materials, Vol. 697, pp. 341-344, 2016

上线时间:

July 2016

关键字:

输出:

价格:

$38.00

* - 通讯作者

[1] N.D. Corbin, Aluminum oxynitride spinel: A review. J Eur Ceram Soc. 5 (1989) 143-154.

[2] J.W. McCauley, P. Patel, M. Chen, et al., AlON: A brief history of its emergence and evolution. J Eur Ceram Soc. 29 (2009) 223-236.

[3] S.S. Kaplan, S. Kurama and G. Gunkaya, Spinel nitrides transparent ceramics. J Eur Ceram Soc. 35 (2015) 3255-3262.

DOI: https://doi.org/10.1016/j.jeurceramsoc.2015.03.033

[4] H.X. Willems, M.M.R.M. Hendrix, G. de With and R. Metselaar, Thermodynamics of Alon I: Stability at lower temperatures . J Eur Ceram Soc. 10 (1992) 327-337.

DOI: https://doi.org/10.1016/0955-2219(92)90088-u

[5] H.X. Willems, G. de With and R. Metselaar, Thermodynamics of Alon III: Stabilization of Alon with MgO . J Eur Ceram Soc. 12 (1993) 43-49.

DOI: https://doi.org/10.1016/0955-2219(93)90069-4

[6] J. Weiss, P. Dreil and L.J. Gauckler, The system Al-Mg-O-N, J Am Ceram Soc. 65 (1982) 68-69.

[7] A. Granon, P. Goeuriot, F. Thevenot , J. Guyader, P. L'Haridon, Y. Laurent, Reactivity in the Al2O3-AlN-MgO system. The MgAlON spinel phase. J Eur Ceram Soc. 13 (1994) 365-370.

DOI: https://doi.org/10.1016/0955-2219(94)90012-4

[8] X.T. Wang, H.Z. Wang, W.J. Zhang, J.L. Sun, and Y.R. Hong, Key Engineering Materials. 226 (2002) 373-378.

[9] W. Dai, W. Lin, A. Yamaguchi, et al., Synthsis of Magnesium Aluminum Oxynitride by Carbothermal Reduction and Nitridation Process. J. Ceram. Soc. Japan, 115 (2007) 42-46.

DOI: https://doi.org/10.2109/jcersj.115.42

[10] X. M. Xie, Y. Wang, J. Q. Qi, et al., Gas-Phase and Solid-State Simultaneous Mechanism for Two-Step Carbothermal AlON Formation. J Eur Ceram Soc. 98 (2015) 1965-(1973).

从Crossref获取数据。
这可能需要一些时间来加载。