Characteristics of the Electroless-Deposited Cu Film as Interconnect on a TaN Diffusion Barrier

摘要:

文章预览

In the present study, thermal properties of the electroless-deposited Cu thin film were investigated. The Cu thin film of good adhesion was successfully deposited on the TaN barrier layer by a electroless deposition method. The multilayered structure of Cu/TaN/Si was prepared by electroless-depositing the Cu thin layer on the TaN diffusion barrier which was deposited by MOCVD on the Si substrate. In order to investigate the effect of post-heat treatment the specimen was annealed in H2 reduction atmosphere. Crystallization and agglomeration of the electroless-deposited Cu film occurred through annealing at H2 atmosphere and resulted in the decrease of film resistance. Thermal stability of Cu/TaN/Si system was maintained up to the annealing temperature of 600°C in H2 atmosphere above which the intermediate compound of Cu-Si was formed through diffusion into the TaN layer

信息:

期刊:

编辑:

S.-G. Kang and T. Kobayashi

页数:

681-684

引用:

J. S. Kim, "Characteristics of the Electroless-Deposited Cu Film as Interconnect on a TaN Diffusion Barrier", Materials Science Forum, Vols. 449-452, pp. 681-684, 2004

上线时间:

March 2004

作者:

输出:

价格:

$38.00