Effects of Core Material on Extrudability of Cu/Pure Al, Cu/Al3003 Clad Composites by Indirect Extrusion

摘要:

文章预览

We investigated about the effects of core material(Pure Al, Al3003) on extrudability such as the maximum extrusion ratio and the bonding strength of Copper Clad Aluminum(CCA) by indirect extrusion. As a results of this experiment, the maximum extrusion ratio of Cu/Al3003 was 38, which was larger than 21.39 of Cu/Al(Cu/pure Al). It was because that the difference of flow stress between copper as the sheath material and Al3003 as the core material was smaller than that of between copper and pure aluminum under the same extrusion temperature of 623K. The bonding strength gradually increased when the extrusion ratio increased, on the other hand, the bonding strength of Cu/Al3003 was higher than that of Cu/Al under same extrusion conditions. The diffusion layer thickness that affected bonding strength was not affected by the kind of core material, but it gradually increased when the extrusion ratio increased. It was thought that Cu/Al3003 had a more intimate diffusion layer than Cu/Al had because the extrusion pressure of Cu/Al3003 was higher than that of Cu/Al under the same extrusion conditions.

信息:

期刊:

主题:

编辑:

Z.Y. Zhong, H. Saka, T.H. Kim, E.A. Holm, Y.F. Han and X.S. Xie

页数:

967-970

引用:

T. K. Jung et al., "Effects of Core Material on Extrudability of Cu/Pure Al, Cu/Al3003 Clad Composites by Indirect Extrusion", Materials Science Forum, Vols. 475-479, pp. 967-970, 2005

上线时间:

January 2005

输出:

价格:

$38.00

[1] Y. Yamaguchi: J. of the Japan Society for Technology of Plasticity, Vol. 15 (1974) pp.723-729.

[2] H. J. Park, K. H. Na: J. of the Korean Society for Technology of Plasticity, (1994) pp.123-130.

[3] C. G. Kang, H. C. Kwon: International Journal of Mechanical Sciences Vol. 44 (2002) pp.247-267.

[4] J. H. Kim, B.K. Suh, H.C. Kwon: J of Korea. Met. Mater. -Int. Vol. 38 (2000) pp.474-479.