Microstructures and Mechanical Properties of Mg-Li-Zn Alloys as Processed by ECAE

摘要:

文章预览

Magnesium alloys and very light metals that can be used for structural application. A variety of Mg-Li-Zn alloys including Mg-11%Li-1%Zn, Mg-9%Li-1%Zn, Mg-9%Li-1%Zn-0.2%Mn, Mg-9%Li-1%Zn-1%Al-0.2%Mn and Mg-9%Li-3%Al-1%Zn-0.2%Mn were processed by equal channel angular extrusion (ECAE) to see how effective is this process in refining the grain structure. After 4 passes of the ECAE process, TEM studied the microstructural diversifications, especially showing the existence of compounds, MgLiZn, MgZn2 and ZnO. The room temperature and high temperature mechanical properties were also investigated. After the ECAE process, the room temperature strength was found enhanced at a modest cost of reduction in elongation.

信息:

期刊:

编辑:

Yafang Han et al.

页数:

225-228

引用:

J. Lee et al., "Microstructures and Mechanical Properties of Mg-Li-Zn Alloys as Processed by ECAE", Materials Science Forum, Vols. 546-549, pp. 225-228, 2007

上线时间:

May 2007

输出:

价格:

$38.00

[1] J. A. Jensen and L. S. Chumbley, Metallurgical and Materials Transactions A, Vol. 29A(1998) 429-435.

[2] K. Higashi and J. Wolfenstine, Materials Letters, Vol. 10 (1991) 329-332.

[3] P. Metenier, G. Gonzales-Doncel, O. A. Ruano, J. Wolfenatine and O. D. Sherby, Materials Science and Engineering, A125 (1990) 195-202.

[4] I. J. Polmear, Materials Transactions, JIM, Vol. 37, No. 1(1996) 12-31.

[5] ASM, Metals Handbook 10th Edition, Vol. 2 (1990) 455-479.

[6] S. Kamado, T. Ashie, Y. Ohshima and Y. Kojima, Materials Science Forum, Vols. 350-351 (2000) 55-62.

[7] Y. Yoshida, L. Cisar, S. Kamado and Y. Kojima: Mater. Trans. JIM 43 (2002) 2419-2423.

[8] J. Y. Wang, Y. H. Chen, Y. L. Yang and S. Lee, Materials Science Forum, Vols. 488-489 (2005) 465-472. 1� m 0. 5� m 100nm.