Fracture Mechanism Analysis of Mg-9Gd-4Y-0.6Zr Alloy

摘要:

文章预览

The fractographs of Mg-9Gd-4Y-0.6Zr alloy specimens which were tensioned at different temperatures were investigated by optical and scanning electron microscopy, respectively. The results showed that different slip systems were activated at different temperatures, which were responsible for varied deformation mechanisms and fracture mechanisms. At 25 °C, the enabled slip systems were few and only the slip systems on basal plane were able to be activated, so cleavage fracture was observed. At −196°Cthe number of enabled slip systems increased, prismatic or pyramidal slip maybe occurred, so that an obvious low-temperature plasticity was observed, while fracture mechanisms were mainly microvoid coalescence fracture with cleavage fracture in local areas. At 250 °C, 300 °C and 350 °C, the multisystem slips on the basal planes, the prismatic planes and the pyramidal planes were able to be activated, while fracture mechanisms were also microviod coalescence fracture. At 400 °C, recrystallization happened, grain-boundary sliding in new fine recrystallized grains made the plastic deformation easy, showing coarse-grain superplasticity phenomenon, and an intergranular shear fracture took place.

信息:

期刊:

编辑:

Yafang Han et al.

页数:

261-266

引用:

X. M. Zhang and Y. Xiao, "Fracture Mechanism Analysis of Mg-9Gd-4Y-0.6Zr Alloy", Materials Science Forum, Vols. 546-549, pp. 261-266, 2007

上线时间:

May 2007

输出:

价格:

$38.00

[1] Y. Xiao, X.M. Zhang, J.M. Chen and H. Jiang: Chinese Journal of Nonferrous Metals, Vol. 16 (2006), p.709.

[2] X.M. Zhang, Y. Xiao, J.M. Chen and H. Jiang: Chinese Journal of Nonferrous Metals, Vol. 16 (2006), p.518.

[3] M.E. Drits, Z.A. Sviderkaya and L.L. Rokhlin: Metalloved. Term. Obrab. Met. Vol. 21 (1979), p.62.

[4] M.E. Drits, L.L. Rokhlin and N.I. Nikitina: Izvestiya Akademii Nauk SSSR, Metally Vol. 5 (1983), p.215.

[5] L.L. Rokhlin and N.I. Nikitina: Z. Metalkd. Vol. 85 (1994), p.819.

[6] I.A. Anyanwu, S. Kamado and Y. Kojima: Mater. Trans. JIM Vol. 42 (2001) p.1206.

[7] I.A. Anyanwu, S. Kamado and Y. Kojima: Mater. Trans. JIM Vol. 42 (2001) p.1212.

[8] E.F. Emley: Principles of Magnesium Technology (Pergamon Press, New York 1966).

[9] Z.H. Chen: Magnesium Alloy (Chemical Industry Press, Beijing 2004).

[10] Z.H. Chen: Wrought Magnesium Alloy (Chemical Industry Press, Beijing 2005).

从Crossref获取数据。
这可能需要一些时间来加载。