作者: Rolf Waesche, Carl Paulick, Gabriele Steinborn, V. Richter, M. Werner
摘要: It has been successfully demonstrated that ceramic materials can be joined in the green state without a second phase by using low pressure injection molded parts. The investigation of the joining interface revealed that a high quality interface can be achieved by carefully adjusting the different manufacturing steps. The use of monomodal particle size distribution in the used powder CT3000SG is inferior to a broader particle size distribution obtained by replacing 33% of the finer alumina powder by coarser CT1200SG. In this way the dewaxing process is significantly improved when the wall thickness of the part exceeds 3 mm. The investigation of the mechanical properties of the joined and sintered parts revealed, that the bending strength of the joined specimens achieved about 80 % of the unjoined, monolithic specimens.
207
作者: Micheline dos Reis Araújo, Cynthia M. Gomes, Gabriele Steinborn, Wilson Acchar, Jens Günster
摘要: Water-based suspensions from commercial Tetragonal stabilized zirconia (3Y-TZP) were produced and characterized with different contents of solids and two different dispersants. According to zeta potential measurements, 3Y-TZP particles showed basic surface characteristics and IEP of around 9 when in aqueous media. The critical volume fraction of solids was about 79.6 wt%, which hindered the processing of more concentrated slurries. Rheological measurements confirmed that well dispersed slurries could be obtained with solid content as high as 79.6 wt.%. The results showed that Triton X-114 was an effective dispersant for preparing well stabilized 3Y-TZP suspensions for the layer-wise slurry deposition process.
195
显示3个文章标题中的1到3个