通过作者查论文: Sun Kyu Park

文章题目页数

作者: Jong Woong Kim, Sun Kyu Park, Seung Boo Jung
摘要: Ball shear test was investigated in terms of effects of important test parameters, i.e. shear height and shear speed, with an experimental and non-linear finite element analysis for evaluating the solder joint integrity of area array packages. A Pb-free solder composition was examined in this work: Sn-3Ag-6Bi-2In. The substrate was a common SMD (Solder Mask Defined) type with solder bond pad openings of 460㎛ in diameter. It could be observed that increasing shear height, at fixed shear speed, has the effect of decreasing shear force, while the shear force increased with increasing shear speed at fixed shear height. Too high shear height could cause some bad effects on the test results such as unexpected high standard deviation values or shear tip sliding from the solder ball surface. The low shear height conditions were favorable for screening the type of brittle interfacial failures or the degraded layers in the interfaces.
851
作者: Jong Woong Kim, Sun Kyu Park, Seung Boo Jung
摘要: Ball shear test was investigated in terms of the effects of important test parameter, i.e., shear height, with an experimental and non-linear finite element analysis for evaluating the solder joint integrity of area array packages. The substrate was a common SMD type with solder bond pad openings of 460 ㎛ in diameter. It was observed that increasing the shear height, at a fixed shear speed, has the effect of decreasing the shear force. The high shear height could cause some bad effects on the test results such as unexpected high standard deviation values or shear tip sliding from the solder ball surface. The low shear height conditions were favorable for screening the type of brittle interfacial fractures or the degraded layers in the interfaces.
269
显示2个文章标题中的1到2个